PEI 1010R-GY8D115 SABIC INNOVATIVE US

ULTEM™

food

High temperature resistan,enhance,Flame retardant,transparent

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE US/1010R-GY8D115
Rockwell hardness	M-Scale	ASTM D785	109

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/1010R-GY8D115
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	207 °C
Hot deformation temperature		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	198 °C
Linear coefficient of thermal expansion	-20 to 150°C，Flow	ASTM E831	5.6E-5 cm/cm/°C
RTI		UL 746	170 °C
RTI Elec		UL 746	170 °C
RTI Imp		UL 746	170 °C
thermal conductivity		ASTM C177	0.22 W/m/K
Vicat softening temperature		ASTM D15255	218 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/1010R-GY8D115
Bending modulus	100 mm Span	ASTM D790	3510 Mpa
bending strength	Yield, 100 mm Span	ASTM D790	165 Mpa
elongation	Yield	ASTM D638	7.0 %
elongation		Break	ASTM D638	60 %
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0 mg
Tensile modulus		ASTM D638	3580 Mpa
tensile strength	Yield	ASTM D638	110 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/1010R-GY8D115
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index		UL 746	PLC 4
Dielectric constant	1 kHz	ASTM D150	3.15
Dielectric strength	1.60 mm, in Air	ASTM D149	33 KV/mm
Dielectric strength		1.60 mm, in Oil	ASTM D149	28 KV/mm
Dissipation factor	2.45 GHz	ASTM D150	2.5E-3
Dissipation factor		1 kHz	ASTM D150	1.3E-3
High arc combustion index		UL 746	PLC 3
High voltage arc tracing rate		UL 746	PLC 2
Hot wire ignition		UL 746	PLC 1
Volume resistivity		ASTM D257	1.0E+17 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/1010R-GY8D115
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	18 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.25 %
Water absorption rate		Equilibrium, 23°C	ASTM D570	1.3 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/1010R-GY8D115
Dart impact	23°C	ASTM D3029	33.0 J
Reverse notch impact	3.20 mm	ASTM D256	1500 J/m
Suspended wall beam without notch impact strength	23°C	ASTM D4812	1300 J/m

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/1010R-GY8D115
Extreme Oxygen Index		ASTM D2863	44 %
UL flame retardant rating	3.0 mm	UL 94	5VA
UL flame retardant rating		0.75 mm	UL 94	V-0

injection	Test Condition	Test Method	SABIC INNOVATIVE US/1010R-GY8D115
Back pressure			0.300 to 0.700 Mpa
drying temperature			150 °C
drying time			4.0 to 6.0 hr
Exhaust hole depth			0.025 to 0.076 mm
Mold temperature			135 to 165 °C
Processing (melt) temperature			350 to 400 °C
Screw speed			40 to 70 rpm
Spray nozzle temperature			345 to 400 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			345 to 400 °C
Temperature at the rear of the barrel			330 to 400 °C
Temperature in the middle of the barrel			340 to 400 °C