Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-797 TAIWAN CHIMEI
POLYLAC®
Electronic field、Electrical field
High gloss
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-797
Melt mass flow rate
ASTM D1238/ISO 1133
g/10min
1
Melt mass flow rate
200℃*5kg
ASTM D1238
g/10min
0
Melt mass flow rate
200℃*10kg
ISO 1133
g/10min
1
Mechanical performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-797
tensile strength
降伏点
ASTM D638
kg/cm2
4
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
Rockwell hardness
ASTM D785
R scale
R
Flexural elasticity
ASTM D790
kg/cm2
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
6
bending strength
ASTM D790
kg/cm2
6
Impact strength of cantilever beam gap
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
2
Impact strength of cantilever beam gap
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Elongation rate
ASTM D638
%
5
IZOD impact strength
1/4"切口
ASTM D256
Kg/cm.cm
3
IZOD impact strength
1/8"切口
ASTM D256
Kg/cm.cm
4
Thermal performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-797
Hot deformation temperature
ASTM D648
°C
8
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
9
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
8
vicat softening point
ASTM D1525/ISO R306
℃（℉）
1
vicat softening point
ASTM D1525
°C
1