TSU InnoTooling™ IE-644-02 Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Innovative Polymers, Inc./InnoTooling™ IE-644-02 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 320 J/m |
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTooling™ IE-644-02 |
|---|---|---|---|
| Viscosity | 固化时间5 | 40 hr | |
| 25°C4 | 3.7 Pa·s | ||
| GelTime | 20to30 min | ||
| 25°C2 | 0.10 Pa·s | ||
| 25°C3 | 3.0 Pa·s |
| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./InnoTooling™ IE-644-02 |
|---|---|---|---|
| Thermosetting components | 脱模时间 | 240to480 min | |
| 硬化法 | 按重量计算的混合比:25按容量计算的混合比:26 | ||
| 树脂 | 按重量计算的混合比:100按容量计算的混合比:100 |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTooling™ IE-644-02 |
|---|---|---|---|
| tear strength | ASTM D624 | 26.3 kN/m | |
| elongation | 断裂 | ASTM D638 | 190 % |
| tensile strength | ASTM D638 | 6.89 MPa | |
| Shore hardness | ShoreA | ASTM D2240 | 75to85 |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./InnoTooling™ IE-644-02 |
|---|---|---|---|
| density | Hardener | 1.09 g/cm³ | |
| 基体树脂 | 1.13 g/cm³ | ||
| Cured | 1.10 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 0.40 % |