Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET X7509HP SABIC INNOVATIVE US
XYLEX™
Electronic and electrical
High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X7509HP |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 77.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 kJ/m² |
| 23°C | ISO 180/1A | 9.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X7509HP |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.3 % |
| tensile strength | 断裂 | ASTM D638 | 63.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.8 % |
| tensile strength | 断裂 | ISO 527-2/50 | 62.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2300 Mpa |
| Tensile modulus | ASTM D638 | 2150 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 95.0 Mpa |
| elongation | 断裂 | ASTM D638 | 140 % |
| bending strength | ISO 178 | 92.0 Mpa | |
| Flexural modulus | ISO 178 | 2260 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 60.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 130 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X7509HP |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.60 % |
| melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 12 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.050 % |
| 饱和,23°C | ISO 62 | 0.12 % | |
| Melt volume flow rate | 265°C/2.16kg | ISO 1133 | 11.5 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X7509HP |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 119 °C |
| vicat | ASTM D152511 | 126 °C | |
| Heat distortion temperature | 1.8MPa,未退火,100mm跨距9，HDT | ISO 75-2/Ae | 106 °C |
| 1.8MPa,未退火,64.0mm跨距10，HDT | ISO 75-2/Af | 108 °C | |
| vicat | -- | ISO 306/B120 | 126 °C |
| Linear coefficient of thermal expansion | MD：23to60°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C | |
| MD：-40to40°C | ISO 11359-2 | 6.8E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 125 °C |
| Linear coefficient of thermal expansion | TD：-40to40°C | ISO 11359-2 | 6.8E-05 cm/cm/°C |
| TD：23to60°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 106 °C |