Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
EHMWPE Quadrant EPP TIVAR® 88-2 ESD Mitsubishi Chemical Advanced Materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® 88-2 ESD |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256A | 无断裂 |
| Supplementary Information | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® 88-2 ESD |
|---|---|---|---|
| limiting pv value | 内部方法 | 0.0701 MPa·m/s |
| hardness | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® 88-2 ESD |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 64 |
| Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® 88-2 ESD |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+5到1.0E+9 ohms |
| Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® 88-2 ESD |
|---|---|---|---|
| tensile strength | 极限 | ASTM D638 | 33.1 MPa |
| elongation | 断裂 | ASTM D638 | 200 % |
| bending strength | 屈服 | ASTM D790 | 21.4 MPa |
| Tensile modulus | ASTM D638 | 800 MPa | |
| Flexural modulus | ASTM D790 | 731 MPa | |
| Compression Modulus | ASTM D695 | 552 MPa | |
| compressive strength | 10%应变,23°C | ASTM D695 | 20.0 MPa |
| coefficient of friction | 与钢-静态 | 内部方法 | 0.080 |
| flammability | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® 88-2 ESD |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® 88-2 ESD |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | <0.010 % |
| 24hr | ASTM D570 | <0.010 % | |
| density | ASTM D792 | 0.940 g/cm³ |
| Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® 88-2 ESD |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 46.7 °C |
| Crystallization peak temperature | DSC | ASTM D3418 | 135 °C |
| Linear coefficient of thermal expansion | MD2：-40到149°C | ASTME831 | 3.6E-04 cm/cm/°C |
| Maximum operating temperature LongTerm, Air | 82 °C |