Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO WCP761 BK1006 SABIC INNOVATIVE US
FLEX NORYL™
Wire insulation applicati
Low Specific Gravity、Low water absorption、Non enhanced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE US/WCP761 BK1006
Shore hardness邵氏A,30秒ASTM D224078
filmTest ConditionTest MethodSABIC INNOVATIVE US/WCP761 BK1006
Tear resistance of pantsISO 6383-116.0 N/mm
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/WCP761 BK1006
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
Volume resistivityASTM D2571.3E+16 ohms·cm
dielectric strength2.00mm,inOilIEC 60243-125 KV/mm
relative permittivity1MHzIEC 602502.50
Dissipation Factor1MHzIEC 602502E-03
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/WCP761 BK1006
Flexural modulus100mmSpanASTM D79050.0 Mpa
elongation断裂ASTM D638170 %
Flexural modulusISO 17840.0 Mpa
tensile strength 断裂ASTM D6387.50 Mpa
Tensile strain断裂ISO 527-2/50170 %
tensile strength 断裂ISO 527-2/508.00 Mpa
otherTest ConditionTest MethodSABIC INNOVATIVE US/WCP761 BK1006
characteristic插头应用.阻燃V-0
Color黑色
purposeIT办公
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/WCP761 BK1006
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13775 °C
UL flame retardant rating6.0mmUL 94V-0
Limiting Oxygen IndexISO 4589-224 %
physical property Test ConditionTest MethodSABIC INNOVATIVE US/WCP761 BK1006
melt mass-flow rate250°C/2.16kgASTM D123820 g/10min
Shrinkage rateMD:24小时ASTM D9551.1 %
Water absorption rate23°C,24hrASTM D5700.10 %
melt mass-flow rate210°C/5.0kgASTM D123815 g/10min
Shrinkage rateTD:24hrASTM D9551.1 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/WCP761 BK1006
brittle temperatureASTM D746<-40.0 °C