Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF1130R-71257 SABIC INNOVATIVE NANSHA
LEXAN™
Automotive sector、Thin walled components
heat-resisting、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1130R-71257 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 127 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |
| MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1130R-71257 |
|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 25 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1130R-71257 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2310 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 93.1 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 6.0 % |
| 断裂 | ASTMD638 | 110 % | |
| Tensile Modulus | ASTMD638 | 2370 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 62.1 Mpa |
| 断裂 | ASTMD638 | 65.5 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1130R-71257 |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Haze | 2540µm | ASTMD1003 | 1.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1130R-71257 |
|---|---|---|---|
| Tensile Impact Strength | ASTMD1822 | 378 kJ/m² | |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 54.2 J |