| Supplementary Information | Test Condition | Test Method | Xuchuan Chemical (Suzhou) Co., Ltd/Xuchuan 6002/B-8006N (Sole) |
|---|---|---|---|
| PreheatTemperature | PartA | 50to60 °C | |
| PartB | 50to60 °C | ||
| FOAMING DENSITY | 400to450 kg/m³ | ||
| PreheatTime | PartA | 8.0to10.0 hr | |
| PartB | 8.0to12.0 hr | ||
| AdhesionStrength-Betweensoleandmid-sole | 39.2to58.8 kN/m | ||
| process temperature | PartB | 40to45 °C | |
| PartA | 40to45 °C |
| hardness | Test Condition | Test Method | Xuchuan Chemical (Suzhou) Co., Ltd/Xuchuan 6002/B-8006N (Sole) |
|---|---|---|---|
| Shore hardness | 邵氏A | 59to70 |
| Mechanical properties | Test Condition | Test Method | Xuchuan Chemical (Suzhou) Co., Ltd/Xuchuan 6002/B-8006N (Sole) |
|---|---|---|---|
| WilliamsAbrasion | 60.0to100 cc/php | ||
| RossFlex | -10°C | NoCrack |
| thermosetting | Test Condition | Test Method | Xuchuan Chemical (Suzhou) Co., Ltd/Xuchuan 6002/B-8006N (Sole) |
|---|---|---|---|
| Thermosetting components | 按重量计算的混合比 | 100 | |
| 脱模时间 | 3.0to5.0 min | ||
| EndofRiseTime | 40.0to50.0 sec | ||
| 部件B | 按重量计算的混合比:55到57 | ||
| CreamTime | 6.0to8.0 sec |
| elastomer | Test Condition | Test Method | Xuchuan Chemical (Suzhou) Co., Ltd/Xuchuan 6002/B-8006N (Sole) |
|---|---|---|---|
| tensile strength | 断裂 | 9.00to12.0 MPa | |
| tear strength | 29.0to40.0 kN/m | ||
| elongation | 断裂 | 350to480 % |
| physical property | Test Condition | Test Method | Xuchuan Chemical (Suzhou) Co., Ltd/Xuchuan 6002/B-8006N (Sole) |
|---|---|---|---|
| density | B-8006N:40°C | 1.080to1.200 g/cm³ | |
| 0.800to0.900 g/cm³ | |||
| Viscosity | A-6002:40°C | 1.00to1.40 Pa·s | |
| density | A-6002:40°C | 1.010to1.020 g/cm³ | |
| Viscosity | B-8006N:40°C | 0.800to1.20 Pa·s |