PC/PBT X2500UV-BK1D355BZDD SABIC INNOVATIVE US
XENOY™
Automotive components、Electronic and electrical
High impact、No fill
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-BK1D355BZDD |
|---|---|---|---|
| Thermal Conductivity | ISO8302 | 0.18 W/m/K | |
| Vicat Softening Temperature | -- | ASTMD152512,ISO306/B5012 | 135 °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | 通过 |
| Vicat Softening Temperature | -- | ASTMD152511,ISO306/B5011 | 135 °C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 108 °C |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 8.5E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B120 | 136 °C |
| Linear thermal expansion coefficient | TD:23到80°C | ISO11359-2 | 8.7E-05 cm/cm/°C |
| MD:-40到40°C | ASTME831 | 8E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,64.0mm跨距11 | ISO75-2/Bf | 126 °C |
| 0.45MPa,未退火,64.0mm跨距10 | ISO75-2/Bf | 126 °C | |
| Linear thermal expansion coefficient | MD:23到80°C | ISO11359-2 | 8.2E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/A50 | 145 °C |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距10 | ISO75-2/Af | 108 °C |
| 1.8MPa,未退火,64.0mm跨距11 | ISO75-2/Af | 108 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-BK1D355BZDD |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 95.0 Mpa |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-BK1D355BZDD |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO527-2/50 | 56.0 Mpa |
| 断裂4 | ASTMD638 | 55.0 Mpa | |
| 断裂5 | ASTMD638 | 55.0 Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 100 % |
| 断裂 | ISO527-2/50 | 70 % | |
| Flexural Strength | --7,8 | ISO178 | 80.0 Mpa |
| --6,7 | ISO178 | 80.0 Mpa | |
| Tensile Modulus | -- | ISO527-2/1 | 2200 Mpa |
| Flexural Strength | 屈服,50.0mm跨距6 | ASTMD790 | 79.0 Mpa |
| 屈服,50.0mm跨距5 | ASTMD790 | 79.0 Mpa | |
| Flexural Modulus | --7 | ISO178 | 2150 Mpa |
| --6 | ISO178 | 2150 Mpa | |
| Tensile Elongation | 屈服 | ASTMD638,ISO527-2/50 | 5.0 % |
| Tensile Modulus | --3 | ASTMD638 | 2200 Mpa |
| Tensile Elongation | 断裂4 | ASTMD638 | 80 % |
| 断裂5 | ASTMD638 | 80 % | |
| Tensile Modulus | --4 | ASTMD638 | 2200 Mpa |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 20.0 mg |
| Flexural Modulus | -- | ASTMD790 | 2100 Mpa |
| Tensile Strength | 屈服 | ASTMD638 | 53.0 Mpa |
| 屈服 | ISO527-2/50 | 57.0 Mpa | |
| Flexural Modulus | 50.0mm跨距5 | ASTMD790 | 2150 Mpa |
| 50.0mm跨距6 | ASTMD790 | 2150 Mpa | |
| Flexural Strength | -- | ASTMD790 | 79.0 Mpa |
| Tensile Elongation | 屈服5 | ASTMD638 | 5.0 % |
| 屈服4 | ASTMD638 | 5.0 % | |
| Tensile Strength | 屈服5 | ASTMD638 | 56.0 Mpa |
| 屈服4 | ASTMD638 | 56.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-BK1D355BZDD |
|---|---|---|---|
| Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.50到0.80 % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.20 % |
| Modeling Shrinkage | TD3 | 内部方法 | 0.50到0.80 % |
| Melt Volume flow Rate | 265°C/1.2kg | ISO1133 | 4.00 cm3/10min |
| Modeling Shrinkage | TD2 | 内部方法 | 0.50到0.80 % |
| Melt Mass-Flow Rate | 265°C/2.16kg | ASTMD1238 | 9.0 g/10min |
| Modeling Shrinkage | MD2 | 内部方法 | 0.50到0.80 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.70 % |
| Modeling Shrinkage | MD3 | 内部方法 | 0.50到0.80 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-BK1D355BZDD |
|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 30 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 60.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 50 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-BK1D355BZDD |
|---|---|---|---|
| Glow Wire Flammability Index | 2.7mm | IEC60695-2-12 | 750 °C |
| Flame Rating | 1.5mm,TestingbySABIC | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/X2500UV-BK1D355BZDD |
|---|---|---|---|
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| Volume Resistivity | IEC60093 | >1.0E+14 ohms·cm | |
| Dissipation Factor? | 60Hz | IEC60250 | 2E-03 |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 60Hz | IEC60250 | 3.30 |
| 1MHz | IEC60250 | 3.10 | |
| Dissipation Factor? | 50Hz | IEC60250 | 2E-03 |
| Relative Permittivity | 50Hz | IEC60250 | 3.30 |
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 |