HDPE DMDD-6200 DOW JAPAN
UNIVL™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDOW JAPAN/DMDD-6200
Impact strength of cantilever beam gapASTM D1822210 kJ/m²
hardnessTest ConditionTest MethodDOW JAPAN/DMDD-6200
Shore hardness邵氏DASTM D224059
Basic performanceTest ConditionTest MethodDOW JAPAN/DMDD-6200
melt mass-flow rate190℃/2.16kgASTM D-12380.25 g/10min
190℃/21.6kgASTM D-123823 g/10min
densityASTM D-7920.953 g/cm
Mechanical propertiesTest ConditionTest MethodDOW JAPAN/DMDD-6200
Environmental stress cracking resistance50℃，10% Igepal，F50ASTM D-169350 hr
tensile strength 屈服ASTM D-63826.2 Mpa
elongation at yieldASTM D-6386 %
elongation屈服ASTM D6386.0 %
Impact strength of cantilever beam gapASTM D-1822210 KJ/m
tensile strength 断裂ASTM D63825.5 Mpa
断裂ASTM D-63825.5 Mpa
elongation断裂ASTM D638900 %
Flexural modulus2% SecantASTM D-790B1020 Mpa
Shore hardnessShore DASTM D-224059
tensile strength 屈服ASTM D63826.2 Mpa
elongation at breakASTM D-638900 %
Flexural modulus2%正割ASTM D790B1020 Mpa
physical property Test ConditionTest MethodDOW JAPAN/DMDD-6200
Environmental stress cracking resistance50°C,100%Igepal,F50ASTM D169350.0 hr
melt mass-flow rate190°C/21.6kgASTM D123823 g/10min
190°C/2.16kgASTM D12380.25 g/10min
Thermal performanceTest ConditionTest MethodDOW JAPAN/DMDD-6200
vicatASTM D1525129 °C
melting temperature内部方法132 °C
Crystallization peak temperatureDSC内部方法119 °C
Heat distortion temperature0.45MPa，Unannealed，HDTASTM D-64870 °C
Crystallization peak temperature内部方法119 °C
Heat distortion temperature0.45MPa,未退火，HDTASTM D64870.0 °C
vicatASTM D-1525129 °C
brittle temperatureASTM D746<-76.1 °C