Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GS2010MLR MITSUBISHI THAILAND
IUPILON™
Camera applications
enhance、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/MITSUBISHI THAILAND/GS2010MLR
Melt Volume-Flow Rate (MVR)
300°C/1.2kg
ISO1133
cm3/10min
9
Melt mass flow rate
300°C/1.2kg
ISO1133
g/10min
1
Water absorption rate
饱和,23°C
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/MITSUBISHI THAILAND/GS2010MLR
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
5
Tensile modulus
ISO527-2
Mpa
4
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
3
tensile strength
断裂
ISO527-2
Mpa
7
elongation
断裂
ISO527-2
%
2
Bending modulus
ISO178
Mpa
4
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PC/MITSUBISHI THAILAND/GS2010MLR
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
4
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
6