Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO X1509-A1A3301 ASAHI JAPAN
XYRON™
Automotive interior parts、Industrial machinery
High temperature resistan、Flame retardant、Filler: Filler、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/X1509-A1A3301 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/X1509-A1A3301 |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 3.10 |
| Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| dielectric constant | 1MHz | IEC 60250 | 3.00 |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 3E-03 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/X1509-A1A3301 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 5.0 % |
| bending strength | 23°C | ISO 178 | 95.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 54.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 3600 Mpa |
| flammability | Test Condition | Test Method | ASAHI JAPAN/X1509-A1A3301 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| 1.5mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/X1509-A1A3301 |
|---|---|---|---|
| Shrinkage rate | 2.00mm | 内部方法 | 0.35-0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.060 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/X1509-A1A3301 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 100 °C |
| Linear coefficient of thermal expansion | MD：-30到65°C | ISO 11359-2 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 97.0 °C |