PPO 500H ASAHI JAPAN
XYRON™
Fitness equipment、Sports Equipment
Chemical resistance、Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/500H |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.50-0.70 % | |
| density | ASTM D-792 | 1.06 mg/cm3 | |
| Water absorption rate | ASTM D-570 | 0.06 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/500H |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 83 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2350 kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 2350 Mpa | ||
| bending strength | ASTM D-790 | 83 Mpa | |
| tensile strength | ASTM D-638 | 49 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 40 % | |
| Rockwell hardness | ASTM D785 | R114 | |
| elongation at break | ASTM D-638 | 50 % | |
| tensile strength | ASTM D638/ISO 527 | 49 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/500H |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.06 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| processability | Test Condition | Test Method | ASAHI JAPAN/500H |
|---|---|---|---|
| Temperature | 70-100 °C |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/500H |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 120 ℃（℉） |
| UL flame retardant rating | UL 94 | HB |