Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 8391 MED TRINSEO NETHERLANDS
MAGNUM™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/TRINSEO NETHERLANDS/8391 MED
Meltvolume-flowrate
220°C/10.0kg
IEC 60093
cm3/10min
2
Apparent density
ISO60
g/cm³
0
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
2
Melt mass flow rate
230°C/3.8kg
ASTMD1238
g/10min
8
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
2
Shrinkage rate
MD
ASTMD955
%
0
Shrinkage rate
MD
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/TRINSEO NETHERLANDS/8391 MED
Charpynotchedimimpact string
23°C
ISO179/1eA3
kJ/m²
1
Nominal strainatbreak
ISO527-23
%
2
Tensile strength
屈服
ASTMD638
Mpa
4
Tensile modulus
3.20mm,注塑
ISO527-2
Mpa
2
Tensile modulus
ISO527-23
Mpa
2
tensile strength
屈服,3.20mm,注塑
ISO527-2/50
Mpa
4
tensile strength
屈服,3.20mm,注塑
ISO527-2/100
Mpa
4
tensile strength
屈服
ISO527-23
Mpa
4
tensile strength
Break
ASTMD638
Mpa
3
elongation
屈服
ASTMD638
%
2
elongation
屈服,3.20mm,注塑
ISO527-2/50
%
2
elongation
屈服,3.20mm,注塑
ISO527-2/100
%
2
elongation
断裂
ASTMD638
%
8
Bending modulus
ASTMD790
Mpa
2
Bending modulus 6,
3.20mm,InjectionMolded
ISO178
Mpa
2
bending strength
ASTMD790
Mpa
7
Bending strength 6,
3.20mm,InjectionMolded
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/TRINSEO NETHERLANDS/8391 MED
Hot deformation temperature
0.45MPa,未退火
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
9
Hot deformation temperature
1.8MPa
ISO75-23
°C
9
vicat softening point
ASTMD15258
°C
9
vicat softening point
ISO306/B50
°C
9
vicat softening point
50N
ISO3063
°C
9
flammability
Test Condition
Test Method
Unit
ABS/TRINSEO NETHERLANDS/8391 MED
Burning rate
2.00mm
ISO3795
mm/min
6