Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV30H2.0 901510 ENVALIOR WUXI
--
--
30% glass fiber reinforce、Easy to flow、Thermal stability rating
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | ENVALIOR WUXI/BKV30H2.0 901510 |
|---|---|---|---|
| Glass Fiber Content | ISO 3451-1 | 30 % |
| Mechanical properties | Test Condition | Test Method | ENVALIOR WUXI/BKV30H2.0 901510 |
|---|---|---|---|
| Tensile Strain | 2mm/min | ISO 178 | 4.1 % |
| tensile strength | 5mm/min | ISO 527-1,-2 | 170 Mpa |
| Bending stress at 3.5% strain | 2mm/min | ISO 178 | 250 Mpa |
| Tensile modulus | 1mm/min | ISO 527-1,-2 | 9000 Mpa |
| Charpy notch impact strength | -30℃ | ISO 179-1eA | ＜10 kJ/m² |
| Elongation | 5mm/min | ISO 527-1,-2 | 3.2 % |
| bending strength | 2mm/min | ISO 178 | 260 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 8000 Mpa |
| processability | Test Condition | Test Method | ENVALIOR WUXI/BKV30H2.0 901510 |
|---|---|---|---|
| Temperature | ISO 294 | 80 °C | |
| Melt Temperature | ISO 294 | 280 °C | |
| injection speed | ISO 294 | 200 mm/s |
| Thermal performance | Test Condition | Test Method | ENVALIOR WUXI/BKV30H2.0 901510 |
|---|---|---|---|
| Deflection Temperature Under Load? | 8.00MPa | ISO 75-1,-2 | 150 °C |
| Hot deformation temperature method Af | 1.80MPa | ISO 75-1,-2 | 200 °C |