Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 457 SABIC INNOVATIVE US
VALOX™
Plastic bag、Automotive External Parts、Electrical/Electronic App、Home appliance components
Flame retardant、Filler: Glass fiber reinf、six、5% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/457 |
|---|---|---|---|
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 152 °C |
| RTIElec | UL746 | 120 °C | |
| Linear thermal expansion coefficient | MD：60到138°C | ASTME831 | 6.7E-05 cm/cm/°C |
| RTI | UL746 | 140 °C | |
| Evolution Calendar intelligent importer | 120 °C | ||
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 204 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/457 |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 121 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/457 |
|---|---|---|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.060 % |
| Modeling Shrinkage | TD3 | 内部方法 | 0.70到0.90 % |
| Density / Specific Gravity | ASTMD792 | 1.44 g/cm³ | |
| Modeling Shrinkage | TD4 | 内部方法 | 0.90到1.2 % |
| Specific Volume | ASTMD792 | 0.690 cm³/g | |
| Modeling Shrinkage | MD2 | 内部方法 | 0.80到1.0 % |
| MD1 | 0.60到0.80 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/457 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 3520 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 79.3 Mpa |
| Flexural Strength | 断裂,50.0mm跨距 | ASTMD790 | 124 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/457 |
|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ASTMD256 | 32 J/m |
| Unnotched Izod Impact Strength | ASTMD4812 | 270 J/m |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/457 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | 750 °C |
| 3.00mm | 725 °C | ||
| Oxygen Index | ASTMD2863 | 32 % | |
| Flame Rating | 0.711mm | UL94 | V-0 |
| Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 960 °C |
| Flame Rating | 3.00mm | UL94 | 5VA |
| Glow Wire Flammability Index | 3.00mm9 | IEC60695-2-12 | 960 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/457 |
|---|---|---|---|
| Dissipation Factor? | 100Hz | ASTMD150 | 2E-03 |
| Volume Resistivity | ASTMD257 | >5.5E+16 ohms·cm | |
| Dielectric Strength | 1.60mm,inOil | ASTMD149 | 24 KV/mm |
| Dielectric Constant | 100Hz | ASTMD150 | 3.50 |
| Dissipation Factor? | 1MHz | 0.020 | |
| Arc Resistance | ASTMD495 | PLC7 | |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| High Amp Arc Ignition | HAI | PLC 3 | |
| Dielectric Constant | 1MHz | ASTMD150 | 3.40 |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |
| High Voltage Arc Tracking Rate | HVTR | PLC 4 | |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 18 KV/mm |