Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE 22501KJ PCC IRAN
--
film
Smoothness、anticaking、antioxidant、Easy to process、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | PCC IRAN/22501KJ |
|---|---|---|---|
| Blow-upRatio | 2.00到3.00 |
| film | Test Condition | Test Method | PCC IRAN/22501KJ |
|---|---|---|---|
| Secant modulus | 2%正割,MD:25µm,吹塑薄膜 | ASTMD882 | 200 Mpa |
| Elmondov tear strength | TD:25µm,吹塑薄膜 | ASTMD1922 | 460 g |
| Film thickness - tested | 25 µm | ||
| tensile strength | MD:屈服,25µm,吹塑薄膜 | ASTMD882 | 13.0 Mpa |
| Elmondov tear strength | MD:25µm,吹塑薄膜 | ASTMD1922 | 110 g |
| Film Thickness | 15.0到150 µm | ||
| tensile strength | TD:屈服,25µm,吹塑薄膜 | ASTMD882 | 12.5 Mpa |
| elongation | TD:断裂,25µm,吹塑薄膜 | ASTMD882 | 780 % |
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ASTMD882 | 45.0 Mpa |
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTMD882 | 680 % |
| Falling hammer impact | 25µm,吹塑薄膜 | ASTMD1709 | 80 g |
| Secant modulus | 2%正割,TD:25µm,吹塑薄膜 | ASTMD882 | 240 Mpa |
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTMD882 | 30.0 Mpa |
| optical performance | Test Condition | Test Method | PCC IRAN/22501KJ |
|---|---|---|---|
| gloss | 45°,25.0µm,吹塑薄膜 | ASTMD2457 | 38 |
| Haze ratio | 25.0µm,吹塑薄膜 | ASTMD1003 | 21 % |
| physical property | Test Condition | Test Method | PCC IRAN/22501KJ |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 0.95 g/10min |