PEI HU1010-1H1000 SABIC INNOVATIVE US
ULTEM™ 
Medical devices、Medical and nursing suppl
Middle flow、Biocompatibility、Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
RTIUL 746170 °C
Deflection Temperature Under Load?1.8 MPa, 未退火, 6.40 mmASTM D648198 °C
0.45 MPa, 未退火, 6.40 mmASTM D648207 °C
Linear thermal expansion coefficient横向 : -40 到 40°CASTM E8315.0E-5 cm/cm/°C
Vicat Softening Temperature--ISO 306/B50211 °C
--ASTM D152510218 °C
--ISO 306/B120212 °C
RTI ElecUL 746170 °C
Thermal ConductivityASTM C1770.22 W/m/K
Linear thermal expansion coefficient流动 : -40 到 40°CISO 11359-25.0E-5 cm/cm/°C
横向 : -40°CISO 11359-25.0E-5 cm/cm/°C
Deflection Temperature Under Load?1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9ISO 75-2/Af193 °C
RTI ImpUL 746170 °C
Linear thermal expansion coefficient流动 : -20 到 150°CASTM E8315.6E-5 cm/cm/°C
HardnessTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Rockwell HardnessM 级ASTM D785109
InjectionTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Middle Temperature340 到 400 °C
Drying Time4.0 到 6.0 hr
Suggested Shot Size40 到 60 %
Drying Temperature150 °C
Mold Temperature135 到 165 °C
Vent Depth0.025 到 0.076 mm
Suggested Max Moisture0.020 %
Processing (Melt) Temp350 到 400 °C
Rear Temperature330 到 400 °C
Nozzle Temperature345 到 400 °C
Front Temperature345 到 400 °C
Back Pressure0.300 到 0.700 Mpa
Screw Speed40 到 70 rpm
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Melt Volume flow Rate360°C/5.0 kgISO 113325.0 cm3/10min
Melt Mass-Flow Rate337°C/6.6 kgASTM D123818 g/10 min
Moisture Absorption平衡, 23°C, 50% RHISO 620.70 %
平衡, 23°CASTM D5701.3 %
Modeling Shrinkage - Flow3.20 mm内部方法0.50 到 0.70 %
Moisture Absorption饱和, 23°CISO 621.3 %
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Tensile Modulus--ISO 527-2/13200 Mpa
Tensile Elongation断裂 3ASTM D63860 %
断裂ISO 527-2/560 %
Flexural Stress-- 6, 7ISO 178160 Mpa
Tensile Strength屈服 3ASTM D638110 Mpa
Flexural Modulus100 mm 跨距 5ASTM D7903510 Mpa
50.0 mm 跨距 4ASTM D7903420 Mpa
Taber Abrasion Resistance1000 Cycles, 1000 g, CS-17 转轮ASTM D104410.0 mg
Tensile Modulus-- 2ASTM D6383580 Mpa
Tensile Elongation屈服ISO 527-2/56.0 %
Flexural Stress屈服, 50.0 mm 跨距 4ASTM D790174 Mpa
屈服, 100 mm 跨距 5ASTM D790165 Mpa
Tensile Elongation屈服 3ASTM D6387.0 %
Flexural Modulus-- 6ISO 1783300 Mpa
Tensile Strength屈服ISO 527-2/5105 Mpa
断裂 3ASTM D638105 Mpa
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Unnotched Izod Impact Strength23°CASTM D48121300 J/m
Instrumented Dart Impact23°C, Total EnergyASTM D376333.0 J
Gardner Impact23°CASTM D302933.0 J
Reverse Notch Izod Impact3.20 mmASTM D2561200 J/m
FlammabilityTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
UL flame retardant rating0.75 mmUL 94V-0
3.0 mmUL 945VA
Oxygen IndexASTM D286344 %
UL flame retardant rating0.71 mmUL 94V-2
Electrical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/HU1010-1H1000
Volume ResistivityASTM D2571.0E+17 ohms·cm
Hot-wire IgnitionUL 746PLC 1
Dielectric Constant1 kHzASTM D1503.15
Dissipation Factor?1 kHzASTM D1501.3E-3
Arc ResistanceASTM D495PLC 5
Dielectric Strength1.60 mm, in AirASTM D14933 KV/mm
Comparative Tracking IndexUL 746PLC 4
High Amp Arc IgnitionUL 746PLC 3
Dielectric Strength1.60 mm, in OilASTM D14928 KV/mm
Dissipation Factor?2.45 GHzASTM D1502.5E-3
High Voltage Arc Tracking RateUL 746PLC 2