Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT KH2100 KANGHUI LIAONING
--
Electrical field,Electronic field,Automotive sector
Glass fiber reinforced,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | KANGHUI LIAONING/KH2100 |
|---|---|---|---|
| Terminal carboxyl content | Q/KHS001 | <24.0 mol/t |
| thermal performance | Test Condition | Test Method | KANGHUI LIAONING/KH2100 |
|---|---|---|---|
| Melting temperature | Q/KHS001 | >222 °C |
| mechanical properties | Test Condition | Test Method | KANGHUI LIAONING/KH2100 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | >150 % |
| tensile strength | ASTM D638 | 50.0to60.0 Mpa |
| Electrical performance | Test Condition | Test Method | KANGHUI LIAONING/KH2100 |
|---|---|---|---|
| Dielectric strength | 2.00mm | ASTM D149 | >20 KV/mm |
| Physical properties | Test Condition | Test Method | KANGHUI LIAONING/KH2100 |
|---|---|---|---|
| ash content | Q/KHS001 | <300 mg/kg | |
| Color B | Q/KHS001 | 1.00to3.00 | |
| Color L | Q/KHS001 | >95.0 | |
| density | ASTM D792 | 1.30-1.32 g/cm³ | |
| Intrinsic viscosity | Q/KHS001 | 0.99to1.0 dl/g | |
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 23to30 g/10min |
| ParticleMass | Q/KHS001 | 1.90to2.10 g/100pcs | |
| water content | Q/KHS001 | <0.20 wt% |
| impact performance | Test Condition | Test Method | KANGHUI LIAONING/KH2100 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | >39 J/m |