Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 1000R-BR7095 SABIC INNOVATIVE US
ULTEM™
Automotive sector、Electrical field、Electronic field
Glass fiber reinforced、Flame retardant、enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/1000R-BR7095 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 53 J/m |
| 23°C | ASTM D4812 | 1300 J/m | |
| 3.20mm | ASTM D256 | 1600 J/m | |
| Dart impact | 23°C | ASTM D3029 | 36.6 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/1000R-BR7095 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 109 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/1000R-BR7095 |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 1.3E-03 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Volume resistivity | ASTM D257 | 1E+17 ohms·cm | |
| dielectric constant | 1kHz | ASTM D150 | 3.15 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| Dissipation Factor | 2.45GHz | ASTM D150 | 2.5E-03 |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 33 KV/mm |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | PLC 5 | |
| dielectric strength | 1.60mm,在油中 | ASTM D149 | 28 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/1000R-BR7095 |
|---|---|---|---|
| Flexural modulus | 100mmSpan | ASTM D790 | 3520 Mpa |
| Poisson's ratio | ASTM D638 | 0.36 | |
| Tensile modulus | ASTM D638 | 3590 Mpa | |
| elongation | 断裂 | ASTM D638 | 60 % |
| bending strength | Yield,100mmSpan | ASTM D790 | 165 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| tensile strength | 屈服 | ASTM D638 | 110 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/1000R-BR7095 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 0.700 | |
| UL flame retardant rating | 3.0mm | UL 94 | 5VA |
| Limiting Oxygen Index | ASTM D2863 | 47 % | |
| UL flame retardant rating | 0.40mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/1000R-BR7095 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.25 % |
| 平衡,23°C | ASTM D570 | 1.3 % | |
| density | ASTM D792 | 1.27 g/cm³ | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 9.7 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/1000R-BR7095 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 201 °C |
| Linear coefficient of thermal expansion | TD：-20to150°C | ASTME831 | 5.4E-05 cm/cm/°C |
| thermal conductivity | ASTMC177 | 0.22 W/m/K | |
| Linear coefficient of thermal expansion | MD：-20to150°C | ASTME831 | 5.6E-05 cm/cm/°C |
| vicat | ASTM D15255 | 219 °C | |
| RTI Imp | UL 746 | 170 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 210 °C |
| RTI Str | UL 746 | 170 °C | |
| RTI Elec | UL 746 | 170 °C |