PP 30YK270E-10000 SABIC INNOVATIVE SHANGHAI
SABIC®STAMAX
Automotive sector、Application in the automo
Chemical coupling、Low volatility、High impact resistance、High mobility、high strength、High rigidity、Filler: Long glass fiber、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/30YK270E-10000 |
---|---|---|---|
Impact strength of simply supported beam without notch | -30°C,注塑 | ISO 179/1eU | 70 kJ/m² |
23°C,注塑 | ISO 179/1eU | 57 kJ/m² | |
Dart impact | 23°C,总能量 | ISO 6603-2 | 58.0 J/cm |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/30YK270E-10000 |
---|---|---|---|
Flexural modulus | 23°C,注塑 | ISO 178 | 5500 Mpa |
Tensile modulus | 120°C,注塑 | ISO 527-2/1B | 3600 Mpa |
tensile strength | 120°C,注塑 | ISO 527-2/1B | 43.0 Mpa |
bending strength | 23°C,注塑 | ISO 178 | 138 Mpa |
Flexural modulus | 80°C,注塑 | ISO 178 | 3600 Mpa |
bending strength | 80°C,注塑 | ISO 178 | 70.0 Mpa |
Tensile modulus | 23°C,注塑 | ISO 527-2/1B | 6200 Mpa |
tensile strength | 23°C,注塑 | ISO 527-2/1B | 98.0 Mpa |
Tensile modulus | 80°C,注塑 | ISO 527-2/1B | 4400 Mpa |
tensile strength | 80°C,注塑 | ISO 527-2/1B | 60.0 Mpa |
Tensile strain | 断裂,23°C,注塑 | ISO 527-2/1B | 2.3 % |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/30YK270E-10000 |
---|---|---|---|
Linear coefficient of thermal expansion | MD:-30到30°C | ASTM D696 | 5.4E-05 cm/cm/°C |
MD:23到80°C | ASTM D696 | 3.7E-05 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 157 °C |