PA66 FG70G50HSLA BK309 DUPONT GERMANY
Zytel®
Electrical applications、Fitness equipment
Thermal stability、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT GERMANY/FG70G50HSLA BK309 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| -30°C | ISO 179/1eU | 90 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT GERMANY/FG70G50HSLA BK309 |
|---|---|---|---|
| Tensile creep modulus | 1000 hr | ISO 899-1 | -- Mpa |
| Tensile modulus | ISO 527-2 | 17000 Mpa | |
| Tensile stress | 断裂 | ISO 527-2 | 250 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.3 % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT GERMANY/FG70G50HSLA BK309 |
|---|---|---|---|
| Volume resistivity | IEC 62631-3-1 | 1.0E+13 ohms·m | |
| Surface Resistivity | IEC 62631-3-2 | -- ohms |
| flammability | Test Condition | Test Method | DUPONT GERMANY/FG70G50HSLA BK309 |
|---|---|---|---|
| FMVSS flammability | FMVSS 302 | SE | |
| UL flame retardant rating | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB |
| ISO 6452 | 4.0E-4 g | ||
| UL flame retardant rating | 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 24 % |
| Filling analysis | Test Condition | Test Method | DUPONT GERMANY/FG70G50HSLA BK309 |
|---|---|---|---|
| Odor | VDA 270 | 3.00 | |
| Melt density | 1.40 g/cm³ | ||
| Ejection Temperature | 210 °C | ||
| Specific Heat Capacity of Melt | 1870 J/kg/°C | ||
| Thermal Conductivity of Melt | 0.31 W/m/K | ||
| Emission of Organic Compounds | VDA 277 | 6.50 µgC/g |
| physical property | Test Condition | Test Method | DUPONT GERMANY/FG70G50HSLA BK309 |
|---|---|---|---|
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 4.2 % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.2 % | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| 横向流量 | ISO 294-4 | 0.80 % |
| Thermal performance | Test Condition | Test Method | DUPONT GERMANY/FG70G50HSLA BK309 |
|---|---|---|---|
| 流动 | ISO 11359-2 | 1.5E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 262 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 260 °C | |
| vicat | ISO 306/B50 | 255 °C | |
| Glass transition temperature 3 | ISO 11357-2 | 80.0 °C | |
| Melting temperature 3 | ISO 11357-3 | 262 °C | |
| thermal conductivity | 0.46 W/m/K |
| injection | Test Condition | Test Method | DUPONT GERMANY/FG70G50HSLA BK309 |
|---|---|---|---|
| Maximum Screw Tangential Speed | 12 m/min | ||
| Temperature | 50 到 90 °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 hr | ||
| Melt Temperature, Optimum | 295 °C | ||
| Processing (melt) temperature | 285 到 305 °C | ||
| Hold Pressure Time | 3.00 s/mm | ||
| drying temperature | 80 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| pressure holding | 50.0 到 100 Mpa | ||
| Suggested maximum moisture content | 0.20 % | ||
| pressure holding | Drying Recommended | yes |