PA66 105F BK010 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 DUPONT USA 105F BK010

Injection grade

US$ 4,480 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	DUPONT USA/105F BK010
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	4 kg·cm/cm(J/M)ft·lb/in
Tensile modulus		ISO 527-2	3200 Mpa
Tensile strain	Yield	ISO 527-2	4.3 %
Tensile modulus		ASTM D638/ISO 527	3200 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	20 %
Nominal tensile fracture strain		ISO 527-2	24 %
tensile strength	Yield	ISO 527-2	85.0 Mpa
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Bending modulus		ASTM D790/ISO 178	2900 kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	85 kg/cm²(MPa)[Lb/in²]
Supplementary Information	Test Condition	Test Method	DUPONT USA/105F BK010
EmissionofOrganicCompounds		VDA277	6.60 µgC/g
Odor		VDA270	2.50
flammability	Test Condition	Test Method	DUPONT USA/105F BK010
UL flame retardant rating	0.71mm	UL 94	V-2
UL flame retardant rating		1.5mm	IEC 60695-11-10,-20	V-2
Extreme Oxygen Index		ISO 4589-2	27 %
UL flame retardant rating	1.5mm	UL 94	V-2
UL flame retardant rating		0.71mm	IEC 60695-11-10,-20	V-2
FMVSS flammability		FMVSS302	SE
Fogging-G-value	condensate	ISO 6452	0.0 g
Physical properties	Test Condition	Test Method	DUPONT USA/105F BK010
Water absorption rate		ASTM D570/ISO 62	2.7 %
Shrinkage rate		ASTM D955	1.5(流动.3.2mm) %
Shrinkage rate		MD	ISO 294-4	1.3 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	8.5 %
Water absorption rate		Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.7 %
Top out temperature			190 °C
Stickiness		ISO 307	145 cm³/g
Shrinkage rate	TD	ISO 294-4	1.3 %
density		ASTM D792/ISO 1183	1.14
thermal performance	Test Condition	Test Method	DUPONT USA/105F BK010
Hot deformation temperature	HDT	ASTM D648/ISO 75	70 ℃（℉）
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	205 °C
Glass transition temperature		ISO 11357-2	60.0 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04 cm/cm/°C
Combustibility (rate)		UL 94	V-2
Melting temperature			263 ℃（℉）
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
Melting temperature		ISO 11357-3	263 °C
Vicat softening temperature		ISO 306/B50	240 °C
other	Test Condition	Test Method	DUPONT USA/105F BK010
characteristic			PA66.耐候.含细微分散碳黑
impact performance	Test Condition	Test Method	DUPONT USA/105F BK010
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	55 kJ/m²