PA66 105F BK010 DUPONT USA
Zytel®
Electronic and electrical accessories,Automotive components
Photostability,Short molding cycle,Good weather resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/105F BK010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| -30°C | ISO 179/1eU | 55 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/105F BK010 |
|---|---|---|---|
| Odor | VDA270 | 2.50 | |
| Emissions of Organic Compounds | VDA277 | 6.60 µgC/g |
| thermal performance | Test Condition | Test Method | DUPONT USA/105F BK010 |
|---|---|---|---|
| melting temperature | 263 ℃（℉） | ||
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 205 °C | |
| HDT | ASTM D648/ISO 75 | 70 ℃（℉） | |
| vicat | ISO 306/B50 | 240 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Combustibility (rate) | UL 94 | V-2 | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C | |
| melting temperature | ISO 11357-3 | 263 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/105F BK010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3200 Mpa | |
| Elongation at break | ASTM D638/ISO 527 | 20 % | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| Nominal tensile fracture strain | ISO 527-2 | 24 % | |
| tensile strength | 屈服 | ISO 527-2 | 85.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.3 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| tensile strength | ASTM D638/ISO 527 | 85 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 3200 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 2900 kg·cm/cm(J/M)ft·lb/in | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 4 kg·cm/cm(J/M)ft·lb/in |
| Electrical performance | Test Condition | Test Method | DUPONT USA/105F BK010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| other | Test Condition | Test Method | DUPONT USA/105F BK010 |
|---|---|---|---|
| characteristic | PA66.耐候.含细微分散碳黑 |
| Physical properties | Test Condition | Test Method | DUPONT USA/105F BK010 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 2.7 % |
| viscosity number | ISO 307 | 145 cm³/g | |
| shrinkage rate | ASTM D955 | 1.5(流动.3.2mm) % | |
| density | ASTM D792/ISO 1183 | 1.14 | |
| shrinkage rate | TD | ISO 294-4 | 1.3 % |
| Ejection Temperature | 190 °C | ||
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 8.5 % |
| shrinkage rate | MD | ISO 294-4 | 1.3 % |
| Water absorption rate | ASTM D570/ISO 62 | 2.7 % |
| flammability | Test Condition | Test Method | DUPONT USA/105F BK010 |
|---|---|---|---|
| Fogging-G-value | condensate | ISO 6452 | 0.0 g |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | V-2 |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | 0.71mm | IEC 60695-11-10,-20 | V-2 |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| 0.71mm | UL 94 | V-2 |