POM F30-03 MITSUBISHI ENGINEERING JAPAN
Iupital™
Thin walled products
High mobility、Thermal stability、wear resistant、High rigidity、High impact resistance、currency
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F30-03 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.00E+16 Ω | |
| Dissipation Factor | ASTM D150 | 0.007 | |
| Volume resistivity | ASTM D257 | 1E+14 ohm.cm | |
| ASTM D257/IEC 60093 | 1.00E+14 Ω.cm | ||
| dielectric strength | ASTM D149 | 483 v/mil | |
| Surface Resistivity | ASTM D257 | 1E+16 Ohm | |
| dielectric constant | ASTM D150 | 3.7 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F30-03 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 13.2 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638 | 9.04 psi | |
| elongation | 断裂 | ASTM D638 | 50 % |
| Flexural modulus | ASTM D790 | 378 psi | |
| ASTM D790/ISO 178 | 379.999 kg/cm²(MPa)[Lb/in²] | ||
| bending strength | ASTM D790 | 13.2 psi | |
| elongation at break | ASTM D638/ISO 527 | 50 % | |
| Impact strength of cantilever beam gap | ASTM D256 | 1.01 ft.ib/in | |
| Rockwell hardness | ASTM D785 | 80 | |
| tensile strength | ASTM D638/ISO 527 | 90.4 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F30-03 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.02 % | |
| density | ASTM D792/ISO 1183 | 1.14 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 27 g/10min |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/F30-03 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.02 in/in | |
| melt mass-flow rate | ASTM D1238 | 27 g/10min |