Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC APEC 2097 COVESTRO GERMANY
Makrolon® 
Automotive sector,Casters,Medical supplies,Nursing supplies
UV curing,Good demolding performanc,High temperature resistan,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
Ball Pressure TestISO 2039-1130 Mpa
thermal performanceTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B191 °C
1.8 MPa, UnannealedISO 75-2/A172 °C
Linear coefficient of thermal expansionFlow : 23 to 55°CISO 11359-26.5E-5 cm/cm/°C
Across Flow : 23 to 55°CISO 11359-26.5E-5 cm/cm/°C
RTIUL 746150 °C
RTI ElecUL 746150 °C
RTI ImpUL 746130 °C
Vicat softening temperatureISO 306/B120202 °C
mechanical propertiesTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
Bending modulus23°CISO 1782450 Mpa
bending strength23°CISO 178110 Mpa
Nominal tensile fracture strain23°CISO 527-2/50> 50 %
Tensile modulus23°CISO 527-2/12450 Mpa
Tensile strainYield, 23°CISO 527-2/506.9 %
tensile strengthYield, 23°CISO 527-2/5076.0 Mpa
Electrical performanceTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
Compared to the anti leakage trace indexSolution BIEC 60112PLC 4
Solution AIEC 60112PLC 0
Dielectric strength23°C, 1.00 mmIEC 60243-135 KV/mm
Dissipation factor23°C, 100 HzIEC 602501.0E-3
23°C, 1 MHzIEC 602509.0E-3
Relative permittivity23°C, 100 HzIEC 602502.90
23°C, 1 MHzIEC 602502.80
Surface resistivityIEC 600931.0E+16 ohms
Volume resistivity23°CIEC 600931.0E+17 ohms·cm
Physical propertiesTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
density23°CISO 11831.13 g/cm³
melt mass-flow rate330°C/2.16 kgISO 11338.0 g/10 min
Melt Volume Flow Rate (MVR)330°C/2.16 kgISO 11338.00 cm3/10min
Shrinkage rate横向Flow : 2.00 mmISO 294-40.90 %
Flow : 2.00 mmISO 294-40.90 %
Water absorption rateSaturation, 23°CISO 620.30 %
Equilibrium, 23°C, 50% RHISO 620.12 %
impact performanceTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
flammabilityTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
Burning wire flammability indexIEC 60695-2-12800 °C
Extreme Oxygen IndexISO 4589-225 %
UL flame retardant rating1.5 mmUL 94HB
injectionTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
Back pressure10.0 to 20.0 Mpa
Drying Temperature - Dry Air Dryer130 °C
Drying time - Dry Air Dryer2.0 to 4.0 hr
Exhaust hole depth0.025 to 0.050 mm
Mold temperature110 to 150 °C
Processing (melt) temperature330 to 340 °C
Spray nozzle temperature315 to 340 °C
Suggested injection volume30 to 70 %
Suggested maximum moisture content< 0.020 %
Temperature at the front of the material cylinder325 to 335 °C
Temperature at the rear of the barrel315 to 325 °C
Temperature in the middle of the barrel320 to 330 °C
optical performanceTest ConditionTest MethodCOVESTRO GERMANY/APEC 2097
Electrolytic corrosion23°CIEC 60426A1
Refractive indexISO 4891.566
transmissivity1000 μmISO 13468-289.0 %