PLA+ABS LA17C UMG JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UMG JAPAN/LA17C |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 21 kJ/m² |
| hardness | Test Condition | Test Method | UMG JAPAN/LA17C |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 106 |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/LA17C |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 3500 MPa |
| tensile strength | 23°C | ISO 527-2 | 40.0 MPa |
| bending strength | 23°C | ISO 178 | 67.0 MPa |
| physical property | Test Condition | Test Method | UMG JAPAN/LA17C |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.80to1.1 % |
| density | 23°C | ISO 1183 | 1.28 g/cm³ |
| Melt volume flow rate | 200°C/10.0kg | ISO 1133 | 59.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/LA17C |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 78.0 °C |