Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HP2-8H9D375 SABIC INNOVATIVE US
LEXAN™
medical care、medicine
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HP2-8H9D375 |
|---|---|---|---|
| Thermal Conductivity | ISO8302 | 0.20 W/m/K | |
| Specific Heat | ASTMC351 | 1250 J/kg/°C | |
| RTIElec | UL746 | 130 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| RTIStr | UL746 | 130 °C | |
| Vicat Softening Temperature | -- | ISO306/B120 | 141 °C |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 137 °C |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 122 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 129 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 140 °C |
| Thermal Conductivity | ASTMC177 | 0.19 W/m/K | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 133 °C |
| Evolution Calendar intelligent importer | UL746 | 130 °C | |
| Vicat Softening Temperature | ASTMD152510 | 154 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/HP2-8H9D375 |
|---|---|---|---|
| Rockwell Hardness | M计秤 | ASTMD785 | 70 |
| R计秤 | ASTMD785 | 118 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HP2-8H9D375 |
|---|---|---|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Moisture Absorption | 平衡,23°C | ASTMD570 | 0.35 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 18 g/10min |
| Specific Volume | ASTMD792 | 0.830 cm³/g | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 16.0 cm3/10min |
| Moisture Absorption | 平衡,100°C | ASTMD570 | 0.58 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HP2-8H9D375 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2340 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 65.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 130 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 100 % |
| Tensile Modulus | ISO527-2/1 | 2350 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 62.0 Mpa |
| Flexural Modulus | ISO178 | 2300 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 96.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 7.0 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 63.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 6.0 % |
| Flexural Strength | ISO178 | 90.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2370 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 68.0 Mpa |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 10.0 mg |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/HP2-8H9D375 |
|---|---|---|---|
| Index of Refraction | ASTMD542 | 1.586 | |
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Haze | 2540µm | ASTMD1003 | 1.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HP2-8H9D375 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| Gardner Impact | 23°C | ASTMD3029 | 169 J |
| Tensile Impact Strength | ASTMD1822 | 546 kJ/m² | |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 62.0 J |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 12 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HP2-8H9D375 |
|---|---|---|---|
| Oxygen Index | ISO4589-2 | 25 % | |
| Flame Rating | 1.5mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HP2-8H9D375 |
|---|---|---|---|
| Dissipation Factor? | 50Hz | ASTMD150 | 9E-04 |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor? | 60Hz | ASTMD150 | 9E-04 |
| 1MHz | ASTMD150 | 0.010 | |
| 60Hz | IEC60250 | 1E-03 | |
| 50Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 0.010 | |
| Hot-wire Ignition | HWI | UL746 | PLC 2 |
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| High Amp Arc Ignition | HAI | UL746 | PLC 1 |
| Volume Resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 2 |
| Dielectric Constant | 60Hz | ASTMD150 | 3.17 |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Dielectric Constant | 50Hz | ASTMD150 | 3.17 |
| Relative Permittivity | 60Hz | IEC60250 | 2.70 |
| 1MHz | IEC60250 | 2.70 | |
| 50Hz | IEC60250 | 2.70 | |
| Dielectric Constant | 1MHz | ASTMD150 | 2.96 |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 15 KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |