PA66 A 218 V20 SOLVAY SHANGHAI
TECHNYL®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY SHANGHAI/A 218 V20 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY SHANGHAI/A 218 V20 |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 7400 Mpa |
| Tensile strain | 断裂, 23°C | ISO 527-2 | 3.0 % |
| bending strength | 23°C | ISO 178 | 235 Mpa |
| Flexural modulus | 23°C | ISO 178 | 6400 Mpa |
| tensile strength | 断裂, 23°C | ISO 527-2/1A | 150 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY SHANGHAI/A 218 V20 |
|---|---|---|---|
| dielectric strength | 2.00 mm | IEC 60243-1 | 32 KV/mm |
| relative permittivity | IEC 60250 | 3.70 | |
| Dissipation Factor | IEC 60250 | 0.010 | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 1 |
| Surface Resistivity | IEC 60093 | 6.0E+15 ohms |
| other | Test Condition | Test Method | SOLVAY SHANGHAI/A 218 V20 |
|---|---|---|---|
| purpose | IT办公 |
| flammability | Test Condition | Test Method | SOLVAY SHANGHAI/A 218 V20 |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 23 % | |
| Burning wire flammability index | 1.6 mm | IEC 60695-2-12 | 650 °C |
| physical property | Test Condition | Test Method | SOLVAY SHANGHAI/A 218 V20 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.4 % |
| 24 hr, 23°C | ISO 62 | 1.0 % | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.45 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 6.6 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.3 % |
| Thermal performance | Test Condition | Test Method | SOLVAY SHANGHAI/A 218 V20 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/Af | 250 °C |
| injection | Test Condition | Test Method | SOLVAY SHANGHAI/A 218 V20 |
|---|---|---|---|
| Suggested maximum moisture content | 0.20 % | ||
| Temperature in the middle of the barrel | 275 to 285 °C | ||
| Temperature at the rear of the barrel | 270 to 280 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 280 to 290 °C | ||
| Temperature | 70 to 100 °C |