PEI STM1500-1000 SABIC INNOVATIVE US
ULTEM™
Automotive Applications、Electrical applications、Wire and cable applicatio
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/STM1500-1000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 15 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 25 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/STM1500-1000 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 590 Mpa | |
| bending strength | --4 | ISO 178 | 18.0 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 20.0 Mpa |
| bending strength | --5 | ISO 178 | 20.0 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 60.0 mg |
| Flexural modulus | ISO 178 | 475 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| 屈服 | ISO 527-2/50 | 15 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 25.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/STM1500-1000 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 4.7E+14 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 9.1E-03 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 19 KV/mm |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 4 |
| -- | IEC 60112 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/STM1500-1000 |
|---|---|---|---|
| Burning wire flammability index | 3.20mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 48 % | |
| UL flame retardant rating | 1.60mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/STM1500-1000 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | ISO 62 | 0.12 % |
| Melt volume flow rate | 320°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | MD1 | 内部方法 | 1.2-1.4 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/STM1500-1000 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |