Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 5013LS-01 JAPAN POLYPLASTIC
TOPAS®
LCD application、Optical applications
Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/5013LS-01 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 13 kJ/m² |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/5013LS-01 |
|---|---|---|---|
| relative permittivity | 10kHz | IEC 60250 | 2.35 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| relative permittivity | 1kHz | IEC 60250 | 2.35 |
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/5013LS-01 |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 1.7 % |
| Tensile modulus | ISO 527-2/1A/1 | 3200 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 46.0 Mpa |
| optical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/5013LS-01 |
|---|---|---|---|
| transmissivity | ISO 13468-2 | 91.0 % | |
| refractive index | ISO 489 | 1.530 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/5013LS-01 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/5013LS-01 |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.10-0.50 % | |
| Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 48.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.010 % |
| melt mass-flow rate | 260°C/2.16kg | ISO 1133 | 44 g/10min |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/5013LS-01 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 127 °C |
| vicat | ISO 306/B50 | 135 °C | |
| Glass Transition Temperature | ISO 11357-2 | 134 °C |