PC/PET TE-5006F KA02 LG CHEM KOREA
LUPOX®
Electrical components、Laptop case、Electrical applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/TE-5006F KA02 |
|---|---|---|---|
| bending strength | 23°C, 3.20 mm, 注塑 | ASTM D790 | 90.2 Mpa |
| Flexural modulus | 23°C, 3.20 mm, 注塑 | ASTM D790 | 2350 Mpa |
| tensile strength | 屈服, 23°C, 3.20 mm, 注塑 | ASTM D638 | 60.8 Mpa |
| elongation | 断裂, 23°C, 3.20 mm, 注塑 | ASTM D638 | > 100 % |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/TE-5006F KA02 |
|---|---|---|---|
| Volume resistivity | 23°C | ASTM D257 | 1.0E+17 ohms·cm |
| arc resistance | ASTM D495 | PLC 7 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | LG CHEM KOREA/TE-5006F KA02 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | V-0 |
| 1.0 mm | UL 94 | V-0 | |
| 0.75 mm | UL 94 | V-0 | |
| 1.6 mm | UL 94 | V-0 5VB |
| physical property | Test Condition | Test Method | LG CHEM KOREA/TE-5006F KA02 |
|---|---|---|---|
| Shrinkage rate | 23°C, 注塑，Flow | ASTM D955 | 0.60 - 1.0 % |
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.10 % |
| melt mass-flow rate | 265°C/2.16 kg | ASTM D1238 | 14 g/10 min |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/TE-5006F KA02 |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm, 注塑，HDT | ASTM D648 | 110 °C |
| melting temperature | ASTM D3418 | 250 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 120 °C | |
| RTI Elec | UL 746 | 120 °C |
| injection | Test Condition | Test Method | LG CHEM KOREA/TE-5006F KA02 |
|---|---|---|---|
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 250 to 260 °C | ||
| Temperature at the rear of the barrel | 245 to 255 °C | ||
| Processing (melt) temperature | 255 to 270 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 255 to 265 °C | ||
| Temperature | 40 to 80 °C | ||
| Spray nozzle temperature | 260 to 270 °C |