LMDPE CL 508 VERSALIS ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | VERSALIS ITALY/CL 508 |
|---|---|---|---|
| tensile strength | TD:屈服,23µm,铸造薄膜 | ISO 527-3 | 17.0 MPa |
| Tensile modulus | 1%正割,MD:23µm,铸造薄膜 | ISO 527-3 | 300 MPa |
| tensile strength | MD:断裂,23µm,铸造薄膜 | ISO 527-3 | 35.0 MPa |
| Tensile modulus | 1%正割,TD:23µm,铸造薄膜 | ISO 527-3 | 330 MPa |
| Elmendorf tear strength | TD:23.0µm | ISO 6383-2 | 80.0 kN/m |
| Dart impact | 23µm,铸造薄膜 | ISO 7765-1 | 40 g |
| film thickness | 8to50µm | ||
| elongation | MD:断裂,23µm,铸造薄膜 | ISO 527-3 | 660 % |
| Elmendorf tear strength | MD:23.0µm | ISO 6383-2 | 20.0 kN/m |
| film thickness | 23 µm | ||
| tensile strength | MD:屈服,23µm,铸造薄膜 | ISO 527-3 | 16.0 MPa |
| elongation | TD:断裂,23µm,铸造薄膜 | ISO 527-3 | 800 % |
| tensile strength | TD:断裂,23µm,铸造薄膜 | ISO 527-3 | 30.0 MPa |
| Mechanical properties | Test Condition | Test Method | VERSALIS ITALY/CL 508 |
|---|---|---|---|
| coefficient of friction | 与自身-动态,铸造薄膜 | ISO 8295 | >0.50 |
| optical performance | Test Condition | Test Method | VERSALIS ITALY/CL 508 |
|---|---|---|---|
| Haze ratio | 23.0µm,铸造薄膜 | ISO 14782 | 3.5 % |
| gloss | 45°,23.0µm,铸造薄膜 | ASTM D2457 | 84 |
| physical property | Test Condition | Test Method | VERSALIS ITALY/CL 508 |
|---|---|---|---|
| density | ISO 1183 | 0.935 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.7 g/10min |
| Thermal performance | Test Condition | Test Method | VERSALIS ITALY/CL 508 |
|---|---|---|---|
| melting temperature | 内部方法 | 128 °C | |
| brittle temperature | ASTM D746 | <-70.0 °C | |
| vicat | ISO 306/A | 118 °C |