PC 915AU BK1E366T SABIC INNOVATIVE US
LEXAN™
Electrical applications、Lighting applications
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/915AU BK1E366T |
|---|---|---|---|
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 125 °C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ASTMD152510,ISO306/B5010 | 140 °C |
| Heat Deflection Temperature | 1.8MPa,未退火,100mm跨距9 | ISO75-2/Ae | 123 °C |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831,ISO11359-2 | 7E-05 cm/cm/°C |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 134 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 125 °C |
| Flow:-40 to 40°C | ASTME831 | 7E-05 cm/cm/°C | |
| Vicat Softening Temperature | -- | ISO306/B120 | 141 °C |
| Flow:-40 to 40°C | ASTME831,ISO11359-2 | 7E-05 cm/cm/°C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 123 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/915AU BK1E366T |
|---|---|---|---|
| Break | ASTMD638 | 66.0 Mpa | |
| Tensile Strength | 断裂 | ISO527-2/50 | 66.0 Mpa |
| 断裂3 | ASTMD638 | 66.0 Mpa | |
| Yield,50.0mm Span | ASTMD790 | 95.0 Mpa | |
| Tensile Elongation | 断裂 | ISO527-2/50 | 100 % |
| Flexural Stress | 屈服,50.0mm跨距4 | ASTMD790 | 95.0 Mpa |
| --5,6 | ISO178 | 98.0 Mpa | |
| ASTMD638 | 2400 Mpa | ||
| fracture | ISO527-2/50 | 100 % | |
| Tensile Modulus | -- | ISO527-2/1 | 2400 Mpa |
| yield | ISO527-2/50 | 6.0 % | |
| Flexural Modulus | --5 | ISO178 | 2400 Mpa |
| Yield | ASTMD638 | 66.0 Mpa | |
| Tensile Modulus | --2 | ASTMD638 | 2400 Mpa |
| fracture | ISO527-2/50 | 66.0 Mpa | |
| ISO178 | 98.0 Mpa | ||
| Tensile Elongation | 断裂3 | ASTMD638 | 100 % |
| Tensile Strength | 屈服 | ISO527-2/50 | 66.0 Mpa |
| Flexural Modulus | 50.0mm跨距4 | ASTMD790 | 2400 Mpa |
| Break | ASTMD638 | 100 % | |
| Tensile Elongation | 屈服3 | ASTMD638 | 6.0 % |
| Yield | ASTMD638 | 6.0 % | |
| 50.0mm Span | ASTMD790 | 2400 Mpa | |
| Tensile Strength | 屈服3 | ASTMD638 | 66.0 Mpa |
| Tensile Elongation | 屈服 | ISO527-2/50 | 6.0 % |
| yield | ISO527-2/50 | 66.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/915AU BK1E366T |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50到0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 23 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 21.0 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Modeling Shrinkage | MD：--1 | 内部方法 | 0.50到0.70 % |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/915AU BK1E366T |
|---|---|---|---|
| Index of Refraction | ISO489 | 1.586 | |
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/915AU BK1E366T |
|---|---|---|---|
| ASTMD256 | 650 J/m | ||
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 |
| ISO180/1A | 65 kJ/m² | ||
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 12 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 60.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 kJ/m² |
| ISO179/2C | 11 kJ/m² | ||
| ISO179/1eA | 65 kJ/m² | ||
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 无断裂 |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/915AU BK1E366T |
|---|---|---|---|
| Flame Rating | 3.00mm | UL94 | V-0 |
| 3.0mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-2 | |
| 1.50mm | UL94 | V-2 |