LCP E6808 UHF BZ SUMITOMO JAPAN
SUMIKASUPER®
--
Low warpage、Glass fiber reinforced、Good forming performance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | SUMITOMO JAPAN/E6808 UHF BZ |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 3.4 | |
| Dielectric loss | ASTM D150/IEC 60250 | 0.004 |
| Mechanical properties | Test Condition | Test Method | SUMITOMO JAPAN/E6808 UHF BZ |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 350 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 120 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 9400 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 100 % | |
| elongation at break | ASTM D638/ISO 527 | 5.0 % | |
| tensile strength | ASTM D638/ISO 527 | 100 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | SUMITOMO JAPAN/E6808 UHF BZ |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.72 | |
| Water absorption rate | ASTM D570/ISO 62 | 0..02 % |
| processability | Test Condition | Test Method | SUMITOMO JAPAN/E6808 UHF BZ |
|---|---|---|---|
| process temperature | 320-340 °C | ||
| pressure | 80-160 Mpa | ||
| Dry conditions | 160 | ||
| screw speed | 中速-高速 rpm | ||
| Temperature | 40-160 °C |
| Thermal performance | Test Condition | Test Method | SUMITOMO JAPAN/E6808 UHF BZ |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | v0 ℃（℉） |
| melting temperature | v0 ℃（℉） |