Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 70G30HSLR NC010 DUPONT USA
Zytel®
Electrical field、Electronic field、Fitness equipment、Automotive sector、Electrical appliances
Thermal stability、Lubricity、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/70G30HSLR NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
| -30°C | ISO 179/1eU | 70 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/70G30HSLR NC010 |
|---|---|---|---|
| Odor | VDA270 | 4.50 | |
| Emissions of Organic Compounds | VDA277 | 3.20 µgC/g |
| Electrical performance | Test Condition | Test Method | DUPONT USA/70G30HSLR NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| dielectric strength | IEC 60243-1 | 38 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 4.30 |
| Dissipation Factor | 100Hz | IEC 60250 | 7E-03 |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | UL 746 | PLC 1 |
| relative permittivity | 1MHz | IEC 60250 | 4.10 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/70G30HSLR NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10000 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.3 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| tensile strength | 断裂 | ISO 527-2 | 200 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/70G30HSLR NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | SE/B | |
| atomization | F-value(refraction) | ISO 6452 | 95 % |
| G-value(condensate) | ISO 6452 | 3E-04 g | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 24 % | |
| burning rate | 1.00mm | ISO 3795 | 24 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/70G30HSLR NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.0 % |
| Ejection Temperature | 210 °C | ||
| MediumDensity | 1.20 g/cm³ | ||
| SpecificHeatCapacity of Melt | 2290 J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.9 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/70G30HSLR NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 1.3E-05 cm/cm/°C |
| TD：-- | ISO 11359-2 | 8E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 2.6E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 2.6E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.3E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 261 °C |
| vicat | ISO 306/B50 | 250 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 253 °C |
| Linear coefficient of thermal expansion | TD：EffectiveThermalDiffusivity | ISO 11359-2 | 1.1E-07 m²/s |
| Glass Transition Temperature | ISO 11357-2 | 80.0 °C |