Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 100P NC010 DUPON SHANGHAI
Delrin®
Automotive sector、Engine parts、Cam
High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPON SHANGHAI/100P NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 15 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 14 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 14 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 12 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 400 kJ/m² |
| hardness | Test Condition | Test Method | DUPON SHANGHAI/100P NC010 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 88 |
| R计秤 | ISO2039-2 | 119 |
| Supplementary Information | Test Condition | Test Method | DUPON SHANGHAI/100P NC010 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 4.70 µgC/g |
| Electrical performance | Test Condition | Test Method | DUPON SHANGHAI/100P NC010 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 2E+13 ohms | |
| Relative Permittivity | 100Hz | IEC60250 | 3.90 |
| Dissipation Factor | 1MHz | IEC60250 | 5.5E-03 |
| CTI | IEC60112 | 600 V | |
| Volume resistivity | IEC60093 | 1E+14 ohms·cm | |
| dielectric strength | IEC60243-1 | 41 KV/mm | |
| Dissipation Factor | 100Hz | IEC60250 | 3.5E-03 |
| Relative Permittivity | 1MHz | IEC60250 | 3.90 |
| Mechanical properties | Test Condition | Test Method | DUPON SHANGHAI/100P NC010 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 45 % | |
| Bending stress | 3.5%应变 | ISO178 | 77.0 Mpa |
| TensileCreepModule | 1hr | ISO899-1 | 2700 Mpa |
| Tensile stress | 屈服 | ISO527-2 | 71.0 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 25 % |
| Tensile modulus | ISO527-2 | 2950 Mpa | |
| Flexural modulus | ISO178 | 2850 Mpa | |
| Poisson's ratio | ISO527 | 0.35 | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1500 Mpa |
| flammability | Test Condition | Test Method | DUPON SHANGHAI/100P NC010 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| Fogging-F-value | refraction | ISO6452 | 91 % |
| FMVSS flammability | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | 50 mm/min |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB |
| 0.8mm | UL94 | HB | |
| 0.8mm | IEC60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | DUPON SHANGHAI/100P NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.9 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 1.4 % |
| MediumDensity | 1.19 g/cm³ | ||
| melt mass-flow rate | ISO1133 | 2.6 g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 2.20 cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 2.2 % |
| density | ISO1183 | 1.42 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.30 % |
| SpecificHeatCapacity of Melt | 3000 J/kg/°C | ||
| ThermalConductivityofMelt | 0.22 W/m/K |
| Thermal performance | Test Condition | Test Method | DUPON SHANGHAI/100P NC010 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD：-40to23°C | ISO11359-2 | 1E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 155 °C |
| 1.8MPa,未退火 | ISO75-2/A | 95.0 °C | |
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 1.1E-04 cm/cm/°C |
| melting temperature | ISO11357-3 | 178 °C | |
| Linear coefficient of thermal expansion | TD：AnnealingTime-Optional | ISO11359-2 | 30.0 min/mm |
| vicat | -- | ISO306/A50 | 175 °C |
| -- | ISO306/B50 | 160 °C | |
| Linear thermal expansion coefficient | TD：-- | ISO11359-2 | 1.1E-04 cm/cm/°C |
| TD：-40to23°C | ISO11359-2 | 1E-04 cm/cm/°C | |
| Linear coefficient of thermal expansion | TD：AnnealingTemperature | ISO11359-2 | 160 °C |