POM S 9364 XAP2 CELANESE USA
HOSTAFORM®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/S 9364 XAP2 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/S 9364 XAP2 |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 16 % |
| Tensile modulus | ISO 527-2/1A/1 | 1650 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 1550 Mpa |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 43.0 Mpa |
| physical property | Test Condition | Test Method | CELANESE USA/S 9364 XAP2 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 4.00 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.5 % |
| MD | ISO 294-4 | 1.6 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.80 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/S 9364 XAP2 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 140 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.1E-04 cm/cm/°C |