EAA 5990 STYRON US
PRIMACOR™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
EAA/STYRON US/5990
Content of comonomer
内部方法
%
2
Melt mass flow rate
125°C/2.16kg2
ASTMD1238,ISO1133
g/10min
6
Melt mass flow rate
190°C/2.16kg3
ASTMD1238,ISO1133
g/10min
1
Melt mass flow rate
125℃/2.16kg
ASTM D-1238
g/10min
Melt mass flow rate
125℃/2.16kg
ISO 1133
g/10min
Melt mass flow rate
190℃/2.16kg
ASTM D-1238
g/10min
1
Melt mass flow rate
190℃/2.16kg
ISO 1133
g/10min
1
Mechanical performance
Test Condition
Test Method
Unit
EAA/STYRON US/5990
Tensile fracture strength
Compression Molded
ASTM D-638
Mpa
Tensile fracture strength
Compression Molded
ISO 527-2
Mpa
Tensile strain at break
Compression Molded
ASTM D-638
%
Tensile strain at break
Compression Molded
ISO 527-2
%
Tensile modulus -2% Secant
Compression Molded
ASTM D-638
Mpa
Tensile modulus -2% Secant
Compression Molded
ISO 527-2
Mpa
Tensile modulus -2% secant
模压成型
ASTMD638,ISO527-2
Mpa
2
tensile strength
断裂,模压成型
ASTMD638,ISO527-2
Mpa
6
elongation
断裂,模压成型
ASTMD638,ISO527-2
%
3
Thermal performance
Test Condition
Test Method
Unit
EAA/STYRON US/5990
Melting temperature
℃
75
I
Melting temperature
内部方法
°C
7
vicat softening point
ASTMD1525,ISO306
°C
4
vicat softening point
ASTM D-1525
℃
vicat softening point
ISO 306
℃