Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC+ABS TAROBLEND 88 G2 Taro Plast S.p.A.
--
--
Filler, glass fiber reinforced material, 10%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G2 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 90 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 25 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G2 |
|---|---|---|---|
| Flexural modulus | ASTMD790 | 4000 MPa | |
| elongation | 断裂 | ASTMD638 | 5.0 % |
| bending strength | 断裂 | ASTM D790 | 100 MPa |
| Tensile modulus | ASTMD638 | 4000 MPa | |
| bending strength | -- | ISO 178 | 100 MPa |
| tensile strength | 屈服 | ASTMD638 | 70.0 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G2 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| dielectric strength | 2.00mm | ASTM D149 | 24 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 4 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G2 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 650 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 24 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G2 |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 0.29 % |
| density | ASTMD792 | 1.19to1.21 g/cm³ | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.29 % | |
| Shrinkage rate | TD | ASTM D955 | 0.20to0.40 % |
| melt mass-flow rate | 260°C/5.0kg | ASTMD1238 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROBLEND 88 G2 |
|---|---|---|---|
| vicat | -- | ASTMD15254 | 140 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 120 °C |
| ball-indentation hardness | 125°C | VDE0470 | 通过 |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 4E-05 cm/cm/°C |
| Continuous use temperature | IEC 60216 | 100 °C | |
| vicat | -- | ASTMD15255 | 134 °C |