Copolyester Optimum® 2000 RAUH USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | RAUH USA/Optimum® 2000 |
|---|---|---|---|
| Dart impact | ASTM D3763 | 36.2 J | |
| Impact strength of cantilever beam gap | -40°C,3.18mm | ASTM D256 | 无断裂 |
| 23°C,3.18mm | ASTM D256 | 1400 J/m |
| Mechanical properties | Test Condition | Test Method | RAUH USA/Optimum® 2000 |
|---|---|---|---|
| elongation | 断裂,3.18mm | ASTM D638 | 500 % |
| Flexural modulus | 3.18mm | ASTM D790 | 1720 MPa |
| tensile strength | 屈服,3.18mm | ASTM D638 | 48.3 MPa |
| flammability | Test Condition | Test Method | RAUH USA/Optimum® 2000 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | RAUH USA/Optimum® 2000 |
|---|---|---|---|
| density | ASTM D792 | 1.22 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.50to0.80 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 100 g/10min |
| Thermal performance | Test Condition | Test Method | RAUH USA/Optimum® 2000 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 65.6 °C |