LMDPE ICORENE® 1613 USA Schulman ICO Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | USA Schulman ICO Polymers/ICORENE® 1613 |
|---|---|---|---|
| Dart impact | -20°C | 内部方法 | >200 J/cm |
| hardness | Test Condition | Test Method | USA Schulman ICO Polymers/ICORENE® 1613 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 62 |
| Mechanical properties | Test Condition | Test Method | USA Schulman ICO Polymers/ICORENE® 1613 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 750 MPa |
| Tensile modulus | ASTM D638 | 800 MPa | |
| elongation | 断裂,滚塑成形 | ASTM D638 | >1000 % |
| tensile strength | 屈服,23°C,3.20mm,滚塑成形 | ISO 527-1 | 20.0 MPa |
| physical property | Test Condition | Test Method | USA Schulman ICO Polymers/ICORENE® 1613 |
|---|---|---|---|
| density | ASTM D1505 | 0.938 g/cm³ | |
| Environmental stress cracking resistance | 50°C,100%Igepal | ASTM D1693 | >1000 hr |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 4.5 g/10min |
| Thermal performance | Test Condition | Test Method | USA Schulman ICO Polymers/ICORENE® 1613 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 127 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 65.0 °C |
| vicat | ISO 306/A | 117 °C |