PC PC-1100U LOTTE KOREA
HOPELEX
Outdoor applications、Plate
Weather resistance、UV resistance、transparent
TDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/PC-1100U |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | > 100 % |
| bending strength | 屈服 | ASTM D790 | 90.2 Mpa |
| tensile strength | 屈服 | ASTM D638 | 61.8 Mpa |
| Flexural modulus | ASTM D790 | 2350 Mpa |
| optical performance | Test Condition | Test Method | LOTTE KOREA/PC-1100U |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.585 | |
| Haze ratio | ASTM D1003 | < 0.80 % |
| physical property | Test Condition | Test Method | LOTTE KOREA/PC-1100U |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Shrinkage rate | Flow | ASTM D955 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/PC-1100U |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ASTM D648 | 143 °C |
| vicat | ASTM D15255 | 150 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 132 °C |
| injection | Test Condition | Test Method | LOTTE KOREA/PC-1100U |
|---|---|---|---|
| drying time | 4.0 hr | ||
| Suggested maximum material return ratio | 20 % | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 280 to 300 °C | ||
| Temperature at the rear of the barrel | 290 to 310 °C | ||
| Processing (melt) temperature | 290 to 310 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 270 to 290 °C | ||
| Temperature | 60 to 90 °C | ||
| Spray nozzle temperature | 280 to 300 °C |