LCP B230 BK430P JAPAN POLYPLASTIC

LAPEROS®

Metal substitution

Conductive,High rigidity,high strength,Halogen-free,Flame retardant,Carbon fiber reinforced,Special strength and stif,30% carbon fiber reinforc,Conductive,Special strength and stif,30% carbon fiber reinforc,Conductive

Plastic Datasheets

Basic Performance	Test Condition	Test Method	JAPAN POLYPLASTIC/B230 BK430P
density		ISO 1183	1500 kg/m

thermal performance	Test Condition	Test Method	JAPAN POLYPLASTIC/B230 BK430P
Combustibility		UL 94	V-0
Crystallization peak temperature		ISO 11357-1	280 °C
Hot deformation temperature	1.80MPa	ISO 75-1	235 °C
		0.45MPa	ISO 75-1	250 °C
		8.00MPa	ISO 75-1	186 °C
Linear coefficient of thermal expansion	normal	ISO 11359-1	4E-06 cm/cm℃
Linear coefficient of thermal expansion		parallel	ISO 11359-1	1E-06 cm/cm℃
Vicat softening temperature	50℃/h 50N	ISO 306	167 °C

mechanical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/B230 BK430P
Bending modulus	23℃	ISO 178	25500 Mpa
bending strength	23℃	ISO 178	320 Mpa
Charpy Notched Impact Strength	23℃	ISO 179/1eA	6.00 KJ/m
elongation	Break	ISO 527-1	0.70 %
Impact strength of cantilever beam gap	23℃	ISO 180/1A	10.00 KJ/m
Impact strength of simply supported beam without notch	23℃	ISO 179/1eU	15.0 KJ/m
Rockwell hardness		ISO 2039-2	99 M Scale
Suspended wall beam without notch impact strength	23℃	ISO 180/1U	12.0 KJ/m
Tensile modulus		ISO 527-1	31800 Mpa
tensile strength		ISO 527-1	200 Mpa

Electrical performance	Test Condition	Test Method	JAPAN POLYPLASTIC/B230 BK430P
Relative permittivity	1000Hz	IEC 60250	32.0
Surface resistivity		IEC 60093	1E+02 ohms
Volume resistivity		IEC 60093	0.10 ohm.m

Physical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/B230 BK430P
Shrinkage rate	parallel	ISO 2577	0.10 %
Shrinkage rate		normal	ISO 2577	0.0 %