ABS Niuk 20GP17 Shanghai Niuk New Plastic Technology Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Shanghai Niuk New Plastic Technology Co., Ltd./Niuk 20GP17 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 20 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Shanghai Niuk New Plastic Technology Co., Ltd./Niuk 20GP17 |
|---|---|---|---|
| tensile strength | ISO 527-2/50 | 60.0 MPa | |
| Flexural modulus | ISO 178 | 5000 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 2.0 % |
| bending strength | ISO 178 | 100 MPa |
| flammability | Test Condition | Test Method | Shanghai Niuk New Plastic Technology Co., Ltd./Niuk 20GP17 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Shanghai Niuk New Plastic Technology Co., Ltd./Niuk 20GP17 |
|---|---|---|---|
| ash content | ISO 3451 | 17 % | |
| melt mass-flow rate | ISO 1133 | 25 g/10min | |
| Shrinkage rate | TD:3.20mm | ISO 2577 | 0.20to0.30 % |
| density | ISO 1183 | 1.15 g/cm³ | |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.20to0.30 % |
| Thermal performance | Test Condition | Test Method | Shanghai Niuk New Plastic Technology Co., Ltd./Niuk 20GP17 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C |