PC PRL PC-FD2 Polymer Resources Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-FD2 |
|---|---|---|---|
| Dart impact | 3.18mm | ASTM D3029 | >36.2 J |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 800 J/m |
| hardness | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-FD2 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| R计秤 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-FD2 |
|---|---|---|---|
| elongation | 断裂,3.18mm | ASTM D638 | 140 % |
| Flexural modulus | 3.17mm | ASTM D790 | 2310 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 62.1 MPa |
| Break,3.18mm | ASTM D638 | 68.9 MPa | |
| elongation | 屈服,3.18mm | ASTM D638 | 6.5 % |
| bending strength | 3.18mm | ASTM D790 | 95.8 MPa |
| optical performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-FD2 |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| physical property | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-FD2 |
|---|---|---|---|
| Shrinkage rate | TD：3.18mm | ASTM D955 | 0.50to0.70 % |
| density | ASTM D792 | 1.20 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.50to0.70 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 9.0to16 g/10min |
| Thermal performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC-FD2 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 135 °C |
| 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 129 °C | |
| vicat | ASTM D15252 | 152 °C |