Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT Romiloy® 5730/01 ROMIRA GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 5730/01 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 50 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 5730/01 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 1950 MPa |
| tensile strength | 23°C | ISO 527-2/50 | 49.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | >50 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2100 MPa |
| bending strength | 23°C | ISO 178 | 75.0 MPa |
| flammability | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 5730/01 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 5730/01 |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.50to0.70 % |
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 23 g/10min |
| Thermal performance | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 5730/01 |
|---|---|---|---|
| vicat | ISO 306/B50 | 114 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C |