Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP HX TRC 135X/6 LYONDELLBASELL HOLAND
Hostacom
Automotive External Parts、Automotive sector、Application in the automo
High mobility、Low shrinkage、Easy to spray、Demolding、Filler: Mineral filler、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LYONDELLBASELL HOLAND/HX TRC 135X/6 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| -30°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/HX TRC 135X/6 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/50 | 17.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 1350 Mpa |
| Tensile modulus | 23°C | ISO 527-2/50 | 1400 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 550 % |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/HX TRC 135X/6 |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 11 g/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/HX TRC 135X/6 |
|---|---|---|---|
| vicat | ISO 306/A50 | 110 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 95.0 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | DIN 53752 | 4.3E-05 cm/cm/°C |