Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE F01552 SABIC SAUDI
SABIC®
film、Bag
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | SABIC SAUDI/F01552 |
|---|---|---|---|
| Elmendorf tear strength | MD | ASTM D1922 | 4.0 g |
| Secant modulus | 1% 正割, MD : 15 µm, 吹塑薄膜 | ASTM D882 | 1400 Mpa |
| tensile strength | MD : 断裂, 15 µm, 吹塑薄膜 | ASTM D882 | 55.0 Mpa |
| Dart impact | ASTM D1709 | 180 g | |
| tensile strength | MD : 屈服, 15 µm, 吹塑薄膜 | ASTM D882 | 31.0 Mpa |
| TD : 断裂, 15 µm, 吹塑薄膜 | ASTM D882 | 49.0 Mpa | |
| elongation | TD : 断裂, 15 µm, 吹塑薄膜2 | ASTM D882 | 610 % |
| Secant modulus | 1% 正割, TD : 15 µm, 吹塑薄膜 | ASTM D882 | 1700 Mpa |
| Elmendorf tear strength | TD | ASTM D1922 | 40 g |
| elongation | MD : 断裂, 15 µm, 吹塑薄膜1 | ASTM D882 | 400 % |
| tensile strength | TD : 屈服, 15 µm, 吹塑薄膜 | ASTM D882 | 30.0 Mpa |
| physical property | Test Condition | Test Method | SABIC SAUDI/F01552 |
|---|---|---|---|
| density | ASTM D1505 | 0.952 g/cm³ | |
| melt mass-flow rate | 190°C/2.16 kg | ISO 1133 | 0.15 g/10 min |
| 190°C/21.6 kg | ISO 1133 | 16 g/10 min |
| Thermal performance | Test Condition | Test Method | SABIC SAUDI/F01552 |
|---|---|---|---|
| vicat | ASTM D1525 | 125 °C |