Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A305M TORAY JAPAN
Torelina®
Electrical appliances,Sports Equipment,Automotive sector,Electronic field,Electrical field
High temperature resistan,high strength,Flame retardant,Filler: Glass mineral,50% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 40 kJ/m² |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 120 mm |
| hardness | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 122 |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | IEC 60250 | 5.00 |
| dielectric strength | IEC 60243-1 | 24 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric constant | ASTM D150/IEC 60250 | 5 | |
| Volume resistivity | ASTM D257/IEC 60093 | 1014 Ω.cm | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 2E-03 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 220 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.3 % |
| Flexural modulus | ASTM D790/ISO 178 | 190 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 23°C | ISO 178 | 260 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 180 Mpa |
| Flexural modulus | 23°C | ISO 178 | 17000 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 740 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 0.9 % | |
| Rockwell hardness | ASTM D785 | 122 | |
| tensile strength | ASTM D638/ISO 527 | 140 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| characteristic | 高强度.流动性 | ||
| Color | 本色.黑 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.16 % | |
| density | ASTM D792/ISO 1183 | 1.85 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| UL flame retardant rating | 0.35mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.75 % |
| MD:3.00mm4 | 内部方法 | 0.16 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A305M |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 278 °C | |
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | >260 ℃（℉） |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-05 cm/cm/°C |
| melting temperature | 278 ℃（℉） | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 3E-05 cm/cm/°C |